Aluminium Alloys Welding Electrodes
Application & Properties:
Electrode with special covering for welding aluminium-silicon alloys and for joining dissimilar aluminium alloys. In welding, hold electrode perpendicularly to workpiece, with a short arc. Wall thicknesses greater than 10 mm and larger workpieces will require preheating from 150oC - 250oC, Since slag residues are corrosive, they must be completely removed from the weld bead. Electrode serves well as consumable in oxyacetylene welding. The covering being hygroscopic, electrodes must be strored in an absolutely dry location, or redried if required.
Aplikasi & Penggunaan:
Kawat las dengan coating khusus untuk pengelasan paduan aluminium-silikon dan penyambungan 2 jenis aluminium berbeda jenisnya. Waktu mengelas, pertahankan supaya busur api sedekat mungkin. Untuk pengelasan dengan ketebalan lebih dari 10 mm diperlukan pemanasan awal dengan temperatur 150oC - 250oC. Karena terak bersifat korosif, maka alur las harus dibersihkan secara total setelah pengelasan. Kawat las bersifat higroskopik, maka harus disimpan di tempat yang kering atau dioven ulang jika diperlukan.
Standar Internasional:
AWS SFA 5.3: E 4043
DIN 1732 : EL AlSi 5
Kekuatan Mekanik Hasil Las:
Yield strength : 90 N/mm2
Tensile strength : 180 N/mm2
Elongation : 15 %
Komposisi Kimia Hasil Las (%):
Si: 5 Fe: 0,3
Al: Basis
Welding Techniques:
Start by using the upper portion of the amperage range. Feed the electrode quickly and move fast maintaining a very close arc gap. When torch welding allow the flux to indicate when the base metal is at temperature.
Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 110-120oC / 2 jam