KAWAT LAS LION TL 88 AWS SFA 5.1 : E 8018-B2

LION TL 88

TL 88 is an iron powder low hydrogen electrodes. The weld metal contains 1, 25% Cr - 0, 5% Mo that makes electrodes more efficient at 550 degree celcius. with the characters of stable arc, little spatter, complete slag covering, it' s suitable for the welding of steel tube for heat transfer of boiler ( STPA22, 23, A335-p11, P12, A199T11, A213T11-12) , drawing steel ( A387Gr11-12) , cast iron ( A217-WC6) , and forging steels ( A182-F11, F12) .

Typical Chemical Analysis of Deposited Metal ( % ) :
C= 0, 069   Mn= 0, 58   Si= 0, 31   P= 0, 024   S= 0, 005   Cr= 1, 32   Mo= 0, 65

Typical Mechanical Properties of Deposited Metal:
Yield Strength ( N/ mm2) = 643
Tensile Strength ( N/ mm2) = 732
Elongation ( % ) = 27
PWHT= 690 C/ 1 hour



Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION 26 AWS SFA 5.1: E 6013

LION 26 
Mild Steel Welding Electrodes

Application & Properties:
Lion 26 is designed for high efficiency welding. Because of its thin flux coating the welding can be done with good slag removability, shallow penetration, less spatters, and beautiful bead.  Lion 26 is suitable for welding vehicles, steel sheets, and other light structures.

Aplikasi & Penggunaan:
Lion 26 dirancang untuk pengelasan efisiensi tinggi. Karena coating-nya yang tipis, pengelasan memiliki keistimewaan: pelepasan terak yang sangat mudah, penetrasi dalam, percikan las sedikit, alur las halus. Lion 26 sangat baik untuk pengelasan kendaraan bermotor, pelat baja, dan konstruksi.

Standar Internasional:
AWS SFA 5.1:  E 6013
JIS Z 3211 :  D 4313
DIN 1913 :  E 43 21 R 3
EN 499 :  E 35 0 R 12

Kekuatan Mekanik Hasil Las:
Yield strength : 450 N/mm2
Tensile strength : 520 N/mm2
Elongation : 25 %
Impact Charpy (0oC) : 72 J

Komposisi Kimia Hasil Las (%):
C: 0,08   P: 0,012
Mn: 0,45   S: 0,009
Si: 0,18

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 200oC / 1 jam

Penggunaan Arus yang Direkomendasikan ( AC atau DC+/- )

Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION 27 AWS SFA 5.1: E 6019

LION 27 
Mild Steel Welding Electrodes

Application & Properties:
Lion 27 is suitable for butt or fillet welding of mild steel (20 mm less) in all positions. It is hard to cause slag inclusion and lustrous bead can be obtained.  The weld metal  has good crack resistance,  good tensile strength and excellent toughness.

Aplikasi & Penggunaan:
Lion 27 sangat cocok untuk pengelasan butt dan fillet dari mild steel pada segala posisi.  Inklusi tidak mungkin terjadi dan hasil lasnya sangat baik. Hasil pengelasan memiliki ketahanan terhadap retak yang baik, tensile strength yang tinggi, serta keuletan yang sempurna.

Standar Internasional:
AWS SFA 5.1:  E 6019
JIS Z 3211 :  D 4301
DIN 1913 :  E 43 32 AR 7
EN 499 :  E 35 0 RA 12

Kekuatan Mekanik Hasil Las:
Yield strength : 420 N/mm2
Tensile strength : 460 N/mm2
Elongation : 28 %
Impact Charpy (-20oC) : 69 J

Komposisi Kimia Hasil Las (%):
C: 0,08   P: 0,014
Mn: 0,45   S: 0,008
Si: 0,08

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 200oC / 1 jam

Penggunaan Arus yang Direkomendasikan ( AC atau DC+/- )

Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION TL 36 AWS SFA 5.1: E 7016

LION TL 36
High Tensile Strenght Welding Electrodes


Application & Properties:
TL 36  is a low hydrogen type electrode  for  welding high tensile steel. The welding can be done with stable arc, less spatters, good slag removability, good slag covering and good X-Ray soundness. It's suitable for low alloy steels, medium carbon steels, heavy steel plates, cast steels and steels of poor weldability.

Aplikasi & Penggunaan:
TL 36 adalah kawat las low hydrogen untuk pengelasan baja berkekuatan tinggi. Pengelasan memiliki kestabilan nyala api yang sangat baik, spatter yang rendah, pelepasan terak  yang mudah, dan performa X-ray yang baik. Sangat cocok untuk baja karbon rendah, baja karbon sedang, pelat baja, ancuran, dan baja yang sulit dilas.

Standar Internasional:
AWS SFA 5.1:  E 7016
JIS Z 3212 :  D 5016
DIN 1913 :  E 51 44 B10
EN 499 :  E 42 2 B12 H10

Kekuatan Mekanik Hasil Las:
Yield strength : 490 N/mm2
Tensile strength : 560 N/mm2
Elongation : 31 %
Impact Charpy (-29oC) : 132 J

Komposisi Kimia Hasil Las (%):
C: 0,08   P: 0,012
Mn: 1,00   S: 0,008
Si: 0,53

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 200oC / 2 jam

Penggunaan Arus yang Direkomendasikan ( AC atau DC+/- )


Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION TL 77 AWS SFA 5.1: E 7018

LION TL 77
High Tensile Strenght Welding Electrodes
 

Application & Properties:
TL 77 is a low hydrogen type electrode for the welding of 490 N/mm2 grade  high tensile steel.  The welding  can be done with high deposition rate, good X-Ray soundness and mechanical properties. It is especially suitable for nuclear power stations, petroleum chemical plants, and heavy steel plates.

Aplikasi & Penggunaan:
TL 77 adalah kawat las low hydrogen untuk pengelasan baja berkekuatan 490 N/mm2. Pengelasan memiliki laju deposisi yang tinggi, performa x-ray yang baik, kekuatan mekanik yang baik. Sangat cocok untuk pengelasan pembangkit listrik tenaga nuklir, pabrik petrokimia, dan pelat baja.

Standar Internasional:
AWS SFA 5.1:  E 7018
JIS Z 3212 :  D 5016
DIN 1913 :  E 51 44 B10
EN 499 :  E 42 3 B32 H10

Kekuatan Mekanik Hasil Las:
Yield strength : 510 N/mm2
Tensile strength : 590 N/mm2
Elongation : 29 %
Impact Charpy (-29oC) : 162 J

Komposisi Kimia Hasil Las (%):
C: 0,08   P: 0,020
Mn: 1,00   S: 0,010
Si: 0,60

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 200oC / 2 jam

Penggunaan Arus yang Direkomendasikan ( AC atau DC+/- )

Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION TL 308 AWS SFA 5.4: E 308-16

LION TL 308
Stainless Steel Welding Electrodes

Application & Properties:
The weld metal  of  TL 308 ia an austenite microstructure  which contains limited delta ferrite. It is suitable for the welding of AISI-304, 304L steel, AISI-301 steel, and AISI-302 steel in all positions.

Aplikasi & Penggunaan:
Hasil kawat las TL 308 memiliki struktur-mikro: austenite yang mengandung delta ferrite yang terbatas. Sangat cocok untuk pengelasan stainless steel AISI 304, 304L, 301, 302 pada segala posisi.

Standar Internasional:
AWS SFA 5.4:  E 308-16
JIS Z 3221 :  D 308-16
DIN 8556 :  E 19 9 R 26
EN 1600 :  E 19 9 R 12

Kekuatan Mekanik Hasil Las:
Tensile strength : 570 N/mm2
Elongation : 45 %

Komposisi Kimia Hasil Las (%):
C: 0,05   Cr:19,38   P: 0,014
Mn: 1,30   Ni: 10,05   S: 0,008
Si: 0,35

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 200oC / 2 jam

Penggunaan Arus yang Direkomendasikan ( AC atau DC+ )
 
Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION TL 308L AWS SFA 5.4: E 308L-16

LION TL 308L
Stainless Steel Welding Electrodes

Application & Properties:
TL 308L is a lime titania type electrode which has excellent usability and weldability.  As its weld metal has extra low carbon austenitic structure, its intergranular corrosion resistibility is especially good than 308 type electrodes.

Aplikasi & Penggunaan:
TL 308L adalah kawat las type lime-titania yang memilki karakteristik pengelasan yang sangat baik. Hasil lasnya memiliki kandungan karbon yang rendah dengan struktur austenite. Ketahanannya  terhadap  korosi intergranular  lebih baik dibandingkan dengan type 308.

Standar Internasional:
AWS SFA 5.4:  E 308L-16
JIS Z 3221 :  D 308L-16
DIN 8556 :  E 19 9 L R 26
EN 1600 :  E 19 9 L R 12

Kekuatan Mekanik Hasil Las:
Tensile strength : 570 N/mm2
Elongation : 45 %

Komposisi Kimia Hasil Las (%):
C: 0,03   Cr:19,38   P: 0,014
Mn: 1,30   Ni: 10,05   S: 0,008
Si: 0,35

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 200oC / 2 jam

Penggunaan Arus yang Direkomendasikan ( AC atau DC+ )


Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION TL 316 AWS SFA 5.4: E 316-16

LION TL 316
Stainless Steel Welding Electrodes


Application & Properties:
The weld metal of TL 316 contains proper quantity of ferrite in austenitic structure. The corrosion resistance against sulfuric acid, phosphorous acid is excellent. It is suitable for chemical plants, AISI 316, 316L, and cladding stainless steel, and also be used for joining of different metals such as mild steel with stainless steel, and under laying before hard surfacing.

Aplikasi & Penggunaan:
Hasil kawat las TL 316 memiliki kandungan ferrite yang tinggi dalam struktur austenite. Ketahanannya terhadap asam sulfat dan asam fosfor sangat baik. Sangat cocok untuk pengelasan pada pabrik kimia, serta stainless steel AISI 316 / 316L, dan dapat  juga digunakan untuk menyambung baja yang berbeda jenis seperti mild steel dengan stainless steel, dan juga sebagai layer pada pengelasan hardfacing.

Standar Internasional:
AWS SFA 5.4:  E 316-16
JIS Z 3221 :  D 316-16
DIN 8556 :  E 19 12 2 R 26
EN 1600 :  E 19 12 2 R 12

Kekuatan Mekanik Hasil Las:
Tensile strength : 570 N/mm2
Elongation : 40 %

Komposisi Kimia Hasil Las (%):
C: 0,05   Cr: 19,50   P: 0,016
Mn: 0,60   Ni: 13,20   S: 0,010
Si: 0,51   Mo: 2,30

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 200oC / 2 jam

Penggunaan Arus yang Direkomendasikan ( AC atau DC+ )
 
Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION TL 316L AWS SFA 5.4: E 316L-16

LION TL 316L
Stainless Steel Welding Electrodes

Application & Properties:
TL 316L is a lime titania type stainless steel electrode, which gives an extra low carbon 19% - 13% - 2% Mo austenitic stainless deposited metal. As the carbon content is lower than 316 type, which usability in acid resistance, corrosion resistability and weldability are excellent. The electrode is used in various of chemical plants  and other heavy duty apparatuses.

Aplikasi & Penggunaan:
TL 316L adalah kawat las stainless steel type lime-titania yang memiliki kandungan karbon yang sangat rendah: 19%Cr-3%Ni-2%Mo austenite. Karena kandungan karbonnya lebih rendah dari type 316, maka kawat las cocok digunakan untuk pengelasan tahan asam. Kawat las sangat cocok untuk pengelasan pada pabrik kimia yang memerlukan ketahanan terhadap asam.

Standar Internasional:
AWS SFA 5.4:  E 316L-16
JIS Z 3221 :  D 316L-16
DIN 8556 :  E 19 12 2 L R 26
EN 1600 :  E 19 12 2 L R 12

Kekuatan Mekanik Hasil Las:
Tensile strength : 570 N/mm2
Elongation : 40 %

Komposisi Kimia Hasil Las (%):
C: 0,03   Cr: 19,50   P: 0,016
Mn: 0,60   Ni: 13,20   S: 0,010
Si: 0,51   Mo: 2,30

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 200oC / 2 jam

Penggunaan Arus yang Direkomendasikan ( AC atau DC+ )

Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION TL 309 AWS SFA 5.4 : E 309-16

LION TL 309
Stainless Steel Welding Electrodes

Application & Properties:
The weld metal of  TL 309 contains more Cr & Ni than  TL 308 / TL 308L. The microstructure containing suitable quantity of ferrite, gives it an excellent resistance to hot cracking. It is suitable for welding of dissimilar metals of mild steel and stainless steel, hardening alloy steel and steel with poor weldability.

Aplikasi & Penggunaan:
Hasil pengelasan TL 309 memiliki kandungan Cr & Ni lebih tinggi dari TL 308 / TL 308L. Struktur mikronya mengandung ferrite dan memiliki ketahanan yang sangat baik terhadap keretakan. Sangat cocok untuk menyambung stainless steel dengan mild steel, pengerasan baja paduan dan baja yang sulit dilas.

Standar Internasional:
AWS SFA 5.4 :  E 309-16
JIS Z 3221 :  D 309-16
DIN 8556 :  E 23 12 R 26
EN 1600 :  E 23 12 R 26

Kekuatan Mekanik Hasil Las:
Tensile strength : 580 N/mm2
Elongation : 41 %

Komposisi Kimia Hasil Las (%):
C: 0,05   Cr: 23,52   P: 0,010
Mn: 1,52   Ni: 13,86   S: 0,010
Si: 0,37

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 200oC / 2 jam

Penggunaan Arus yang Direkomendasikan ( AC atau DC+ )


Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION TL 309L AWS SFA 5.4 : E 309L-16

LION TL 309L
Stainless Steel Welding Electrodes

Application & Properties:
 TL 309L is usually used for joining stainless steels to non alloy or low alloy steels. The corrosion  resistance is important in surfacing and is dependent on the composition of the weld metal obtained. It is possible in practice to obtain full resistance to intergranular corrosion due to the low carbon content of the weld metal.

Aplikasi & Penggunaan:
TL 309L sangat cocok untuk pengelasan stainless steel  dengan baja karbon, dimana ketahanan terhadap korosi merupakan prioritas karena komposisi kimia dari hasil las. Kandungan karbonnya rendah dan hasil las memiliki ketahanan terhadap korosi intergranular.

Standar Internasional:
AWS SFA 5.4 :  E 309L-16
JIS Z 3221 :  D 309L-16
DIN 8556 :  E 23 12 L R 26
EN 1600 :  E 23 12 L R 26

Kekuatan Mekanik Hasil Las:
Tensile strength : 580 N/mm2
Elongation : 41 %

Komposisi Kimia Hasil Las (%):
C: 0,03   Cr: 23,52   P: 0,010
Mn: 1,52   Ni: 13,86   S: 0,010
Si: 0,37

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 200oC / 2 jam

Penggunaan Arus yang Direkomendasikan ( AC atau DC+ )


Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION TL 312 AWS SFA 5.4: E 312-16

LION TL 312
Stainless Steel Welding Electrodes

Application & Properties:
The weld metal of TL 312 is a stainless steel which contain more quantities of ferrite than TL 309 / TL 309L. Crack resistance is good.  It is excellent for the welding of dissimilar metals, cladding steel and steels with high hardenability.

Aplikasi & Penggunaan:
Hasil pengelasan TL 312 memiliki kandungan ferrite lebih tinggi dari TL 309 / TL 309L. Ketahanannya terhadap keretakan sangat baik. Sangat cocok untuk pengelasan baja yang berbeda jenisnya, baja yang tidak diketahui jenisnya, dan baja yang memiliki kekerasan yang tinggi.

Standar Internasional:
AWS SFA 5.4:  E 312-16
JIS Z 3221 :  D 312-16
EN 1600 :  E 29 9 R 12

Kekuatan Mekanik Hasil Las:
Tensile strength : 760 N/mm2
Elongation : 29 %

Komposisi Kimia Hasil Las (%):
C: 0,12   Cr: 28,50   P: 0,015
Mn: 1,35   Ni: 8,95   S: 0,010
Si: 0,50

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 200oC / 2 jam

Penggunaan Arus yang Direkomendasikan ( AC atau DC+ )

Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION TL 317 AWS SFA 5.4: E 317-16

LION TL 317
Stainless Steel Welding Electrodes

Application & Properties:
The weld metal of TL 317 contains proper quantity of ferrite in austenitic  structure.  Good corrosion resistance  to  sulfuric acid and organic acid can be obtained due its Mo content. It is suitable for welding of chemical vessels and AISI 317, 317L steel.

Aplikasi & Penggunaan:
Hasil las TL 317 memiliki kandungan ferrite yang tinggi dalam struktur austenite. Ketahanannya terhadap asam sulfat dan asam-asam organik lainnya sangat baik karena kandungan Mo-nya yang tinggi. Sangat cocok untuk pengelasan tanki-tanki kimia dan stainless steel type 317 / 317L, serta pabrik kimia dan sejenisnya.

Standar Internasional:
AWS SFA 5.4:  E 317-16
JIS Z 3221 :  D 317-16
EN 1600 :  E 19 13 4 R 12

Kekuatan Mekanik Hasil Las:
Tensile strength : 580 N/mm2
Elongation : 42 %

Komposisi Kimia Hasil Las (%):
C: 0,05   Cr: 19,60   P: 0,015
Mn: 1,49   Ni: 13,85   S: 0,010
Si: 0,36   Mo: 3,52

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 200oC / 2 jam


Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION TL CAST

Lion TL Cast
Cast Iron Welding Electrodes

Application & Properties:
TL Cast is a low hydrogen type electrode with mild steel core wire. It is designed for the welding of cast iron when machinability  of  deposited metal  is not important.  The welding can be done with stable arc and less porosity. It Has a wide application due to its low  cost  and excellent weldability. It is suitable for repairing cracks or breaks in cast iron.

Aplikasi & Penggunaan:
TL Cast adalah kawat las ancuran (cast iron) dengan kawat inti mild steel. Sangat Cocok untuk pengelasan ancuran (cast iron) yang tidak perlu dibubut.  Pengelasan memiliki kestabilan nyala api yang sangat baik, dan tanpa pori. Aplikasinya sangat luas, harganya relatif rendah, dan hasil pengelasannya sangat baik. Sangat cocok untuk perbaikan keretakan atau kerusakan pada baja ancuran.

Komposisi Kimia Hasil Las (%):
C: 1,60   Si: 1,20   S: 0,006
Mn: 0,45   P: 0,020

Petunjuk pemakaian:
1. Panaskan kawat las sebelum digunakan.
2. Bersihkan material las sebelum dilas.
3. Panaskan material las pada temperatur 200 - 350oC.
4. Gunakan arus sekecil-kecilnya dengan busur las sedekat mungkin.

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 200oC / 2 jam

Penggunaan Arus yang Direkomendasikan (AC atau DC(+))

Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com

KAWAT LAS LION ALCORD Si 5 AWS SFA 5.3: E 4043

 Lion Alcord Si 5
Aluminium Alloys Welding Electrodes

Application & Properties:
Electrode with special covering for welding aluminium-silicon alloys and for joining dissimilar aluminium alloys. In welding, hold electrode perpendicularly to workpiece, with a short arc. Wall thicknesses greater than 10 mm and larger workpieces will require preheating from 150oC - 250oC, Since slag residues are corrosive, they must be completely removed from the weld bead. Electrode serves well as consumable in oxyacetylene welding. The covering being hygroscopic, electrodes must be strored in an absolutely dry location, or redried if required.

Aplikasi & Penggunaan:
Kawat las dengan coating khusus untuk pengelasan paduan aluminium-silikon dan penyambungan 2 jenis aluminium berbeda jenisnya. Waktu mengelas, pertahankan supaya busur api sedekat mungkin. Untuk pengelasan dengan ketebalan lebih dari 10 mm diperlukan pemanasan awal dengan temperatur 150oC - 250oC. Karena terak bersifat korosif, maka alur las harus dibersihkan secara total setelah pengelasan. Kawat las bersifat higroskopik, maka harus disimpan di tempat yang kering atau dioven ulang jika diperlukan.

Standar Internasional:
AWS SFA 5.3:  E 4043
DIN 1732 :  EL AlSi 5

Kekuatan Mekanik Hasil Las:
Yield strength : 90 N/mm2
Tensile strength : 180 N/mm2
Elongation : 15 %

Komposisi Kimia Hasil Las (%):
Si: 5   Fe:  0,3
Al: Basis

Welding Techniques:
Start by using the upper portion of the amperage range. Feed the electrode quickly and move fast maintaining a very  close arc gap. When torch welding allow the flux to indicate when the base metal is at temperature.

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang: 110-120oC / 2 jam

Penggunaan Arus yang Direkomendasikan (DC+)


Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com


KAWAT LAS LION ALCORD Si 12 DIN 1732 : EL AlSi 12

Lion Alcord Si 12
Aluminium Alloys Electrodes

Application & Properties:
Electrode with special covering for welding aluminium-silicon alloys and for joining dissimilar aluminium alloys. In welding, hold electrode perpendicularly to workpiece, with a short arc. Wall thicknesses greater than 10 mm and larger workpieces will require preheating from 150oC - 250oC, Since slag residues are corrosive, they must be completely removed from the weld bead. Electrode serves well as consumable in oxyacetylene welding. The covering being hygroscopic, electrodes must be strored in an absolutely dry location, or redried if required.

Aplikasi & Penggunaan:
 Kawat las dengan coating khusus untuk pengelasan paduan aluminium-silikon dan penyambungan 2 jenis aluminium berbeda jenisnya. Waktu mengelas, pertahankan supaya busur api sedekat mungkin. Untuk pengelasan dengan ketebalan lebih dari 10 mm diperlukan pemanasan awal dengan temperatur 150oC - 250oC. Karena terak bersifat korosif, maka alur las harus dibersihkan secara total setelah pengelasan. Kawat las bersifat higroskopik, maka harus disimpan di tempat yang kering atau dioven ulang jika diperlukan.

Standar Internasional:
DIN 1732 :  EL AlSi 12

Kekuatan Mekanik Hasil Las:
Yield strength : 80 N/mm2
Tensile strength : 180 N/mm2
Elongation : 5 %

Komposisi Kimia Hasil Las (%):
Si: 12   Fe:  0,4
Al: Basis

Welding Techniques:
Start by using the upper portion of the amperage range. Feed the electrode quickly and move fast maintaining a very  close arc gap. When torch welding allow the flux to indicate when the base metal is at temperature

Perhatian:
Hanya gunakan kawat las yang kering!
Pengeringan ulang:110-120oC / 2 jam

Penggunaan Arus yang Direkomendasikan (DC+)

Contact Person:  Setyo Nugroho, ST
No.HP               :  0815 84104675
Telp                   : 021-33038206
Email                 : setyo.marketing@yahoo.com